　　 The black stain is formed in a ceramic crucible (sample boat) and is used in the TOC analysis module of solid samples. How to remove the stain? How to clean ceramic crucible in muffle furnace?

We often encounter the problem of how to clean the ceramic crucible in muffle furnace. Today we Zhengzhou Kejia Electric Furnace Co., Ltd. will solve this problem for you. Please check that alumina or ceramics have been formed with your material at any stage through reaction or diffusion. Any transition metal oxide or rare earth oxide composition, alumina ceramic crucible and material reaction heating. It is generally recommended to try HCl (≥ 25 wt%). If it is ineffective, then it may be worth trying hydrochloric acid + nitric acid (volume ratio 1:1; ≥ 25 wt%), with safety issues, suitable for aqua regia. We will require all of these experiments to be carried out after washing with distilled water. The dry crucible runs slowly at 110 ℃ for 10 hours and heats up to 1000 degrees for the first time. If the marking is due to the organic part of the carbon simply change your boat / crucible in the air slowly up to 1200 degrees Celsius. A slope rate of 2 degrees and a residence time of 10 minutes at 900 degrees would be good enough to eliminate solid carbon deposition in the module.

Prev:Composition and application of CVD system

Next:Application and classification of experimental electric furnace

How to clean ceramic crucible in muffle furnace

Single-Zone Tube Furnace

Multi-Zone Tube Furnace

Rotary Tube Furnace

Vertical Tube Furnace

Slideway Tube Furnace

RTP fast Annealing Furnace

Lab Scale Pyrolysis Furnace

Diffusion Oxidation Tube Furnace

Ultrasonic Spray Pyrolysis Furnace

High temperature high pressure

OLED material purification

400℃-1200℃ Box Furnace

1300℃-1400℃ Box Furnace

1500℃-1700℃ Box Furnace

Bell Type Furnace

Crucible Furnace

Bogie Hearth Furnace

CVD Furnace System

PECVD Furnace System

Roll-to-roll graphene film growth equipment

LP/AP CVD System

Vacuum Sintering Furnace

Vacuum Annealing Furnace

Vacuum Brazing Furnace

Vacuum Tempering Furnace

Vacuum Hot Pressing Furnace

Vacuum Gas Quenching Furnace

Vacuum Carbon Tube Furnace

400℃-1200℃

1300℃-1400℃

1500℃-1700℃

Custom Vacuum Furnace

Custom Box Furnace

Custom Tube Furnace

Zirconia Sintering Furnace

Porcelain Press Furnace

Vacuum Porcelain Furnace

Dental Dewaxing Furnace

Lab Vacuum Equipment

Vacuum System and Gas Mixing System

Reactors

Induction Furnace

Vacuum Oven

Accessories and Consumables